CERAMIC MICRO GRINDING MEDIA |
||||
| HOME>>PRODUCT INFO>>ZIRCONIA-BASED BEADS SZS | |||||
| ZIRCONIA-BASED BEADS |
|
Composition (wt%) | ZrO2+HfO2 | ≥65.0 | |
| SZS | SiO2 | ≤35.0 | |||
| Specific Density | ≥4.0 g/cm3 | ||||
| Bulk Density | ≥2.5 g/cm3 | ||||
| Mohs' hardness | 7.2 | ||||
| Breaking Load | ≥800 N | ||||
| Roudness | ≥95% | ||||
| Opean Porosity | 0% | ||||
| Color | White | ||||
| Surface finish | silky sheen | ||||
| Standard Sizes | Ф0.4 - 5.0 mm | ||||
| Properties: | |||||
| ● Made of a zirconia/silica ceramic blend in a special sintering process. | |||||
| ● High density(≥4.0 g/cm3) insures superior milling efficiency, particularly in medium and high viscosity | |||||
| formulations, improving throughout rates and allowing fewer passes. | |||||
| ● Conditioned, highly polished surface reduces mill and media wear when grinding. | |||||
| ● Fully solid, spherical shape prevents shattering and screen-blinding, also reduces mill and media wear. | |||||
| ● Free from “blowholes”, “snowmen”, “dumbbells” and weak hollow beads. | |||||
| ● Washes quickly, easily and completely. | |||||
| Applications: Minerals, Calcium Carbonate, Titanium Dioxide, Paint, Inks, Pigments, Dyes etc… | |||||
| Standard Size Range: (special sizes are available upon request) | |||||
| Size Range (mm) | Size Range (mm) | ||||
| 0.4-0.6 | 2.0-2.5 | ||||
| 0.6-0.8 | 2.5-3.0 | ||||
| 0.8-1.0 | 3.0-3.5 | ||||
| 1.0-1.2 | 3.5-4.0 | ||||
| 1.2-1.4 | 4.0-4.5 | ||||
| 1.4-1.7 | 4.5-5.0 | ||||
| 1.5-2.0 | |||||